Synthesis and structural characterization of novel,fluorinated poly(phthalazinone ether)s containing perfluorophenylene moieties

The synthesis and structural characterization of a series of novel, fluorinated poly(phthalazinone ether)s containing perfluorophenylene moieties are described. The monomers, 4‐(4′‐hydroxyaryl)phthalazin‐1(2H)‐ones ( 2a – 2d ), were conveniently and efficiently synthesized from phenols and phthalic anhydride in two steps via 2‐(4′‐hydroxybenzoyl)benzoic acids, which were first obtained by the Friedel–Crafts reaction in good yields and with high stereoselectivity and were then converted into 2a – 2d by fusion with hydrazine. All the polymers were prepared by nucleophilic aromatic substitution (S_NAr) polycondensation between the compounds perfluorobiphenyl and 4‐(4′‐hydroxyaryl)phthalazin‐1(2H)‐ones ( 2a ‐ 2d ). The resulting fluorinated polymers were readily soluble in common organic solvents (e.g., CHCl₃, tetrahydrofuran, dimethylformamide, dimethyl sulfoxide, N‐methylpyrrolidone, etc.) at room temperature. Their weight‐average molecular weights and the polydispersities ranged from (7.96–18.25) × 10³ to 1.31–2.71, respectively. Their glass‐transition temperatures varied from 213 to 263 °C. They were all stable up to 390 °C both in air and in argon. The 5% weight‐loss temperatures of these polymers in air and argon ranged from 393–487 to 437–509 °C, respectively. Wide‐angle X‐ray diffraction studies indicated they were all amorphous and could be attributed to the presence of kink nonplanar moiety, phenyl phthalazinone along the polymer backbone. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 925–932, 2004     

Behavior and surface energies of polybenzoxazines formed by polymerization with argon,oxygen, and hydrogen plasmas

Polybenzoxazine (PBZZ) thin films can be fabricated by the plasma‐polymerization technique with, as the energy source, plasmas of argon, oxygen, or hydrogen atoms and ions. When benzoxazine (BZZ) films are polymerized through the use of high‐energy argon atoms, electronegative oxygen atoms, or excited hydrogen atoms, the PBZZ films that form possess different properties and morphologies in their surfaces. High‐energy argon atoms provide a thermodynamic factor to initiate the ring‐opening polymerization of BZZ and result in the polymer surface having a grid‐like structure. The ring‐opening polymerization of the BZZ film that is initiated by cationic species such as oxygen atoms in plasma, is propagated around nodule structures to form the PBZZ. The excited hydrogen atom plasma initiates both polymerization and decomposition reactions simultaneously in the BZZ film and results in the formation of a porous structure on the PBZZ surface. We evaluated the surface energies of the PBZZ films polymerized by the action of these three plasmas by measuring the contact angles of diiodomethane and water droplets. The surface roughness of the films range from 0.5 to 26 nm, depending on the type of carrier gas and the plasma‐polymerization time. By estimating changes in thickness, we found that the PBZZ film synthesized by the oxygen plasma‐polymerization process undergoes the slowest rate of etching in CF₄ plasma. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4063–4074, 2004     

Bio‐based nanocomposites from functionalized plant oils and layered silicate

Some discovery work was done on the synthesis of clay nanocomposites based on renewable plant oils. Functionalized triglycerides, such as acrylated epoxidized soybean oil, maleinized acrylated epoxidized soybean oil, and soybean oil pentaerythritol maleates, combined with styrene were used as the polymer matrix. The miscibility of these monomers and clay organomodifier was assessed by solubility parameters. The formation of nanocomposites was confirmed by both X‐ray data and transmission electron microscopy. The morphology showed a mix of intercalated and partially exfoliated sheets. The flexural modulus increased 30% at only 4 vol % clay content, but there was no significant effect on flexural strength, glass‐transition temperature, and thermal stability. Property enhancement was related to the degree of exfoliation that depends on both the polarity and flexibility of the monomers. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1441–1450, 2004     

溶胶-凝胶法制备小颗粒(Y,Gd)BO_3∶Eu及其表征

用溶胶 凝胶方法制备了平均粒径为 1～ 2 μm的小颗粒、高发射效率的 (Y ,Gd)BO3 ∶Eu红色发射荧光体。用XRD、SEM、粒度分析和PL光谱对荧光体作了表征和研究。常规固相反应合成 (Y ,Gd)BO3 ∶Eu需在 1 2 0 0℃以上才能形成均一的固溶体。而溶胶 凝胶法制取稀土正硼酸盐 80 0℃灼烧已可形成均一的单相 (Y ,Gd)BO3 ∶Eu,在 1 1 0 0℃可得到发光亮度最高的荧光体。它的亮度是常规固相反应于 1 2 0 0℃制得的荧光体的 1 2 0 %。采用溶胶 凝胶法制取 (Y ,Gd)BO3 ∶Eu荧光体 ,可在相当宽的实验条件范围内得到小粒径、窄分布和高亮度的荧光体 ,且有良好的颗粒形貌。     

Synthesis and Photocytotoxicity of Mono-functionalised Porphyrin with Valine Moiety

A mono-funtionalised tetraphenylporphyrin (TPP) bearing valine moiety at the phenyl ring was synthesized for photocytotoxicity examination in four steps, starting from regiospecific mono-nitration of TPP at the phenyl ring. The in vitro photocytotoxicitic effect against SPC-Al adenocarcinona cell line was tested.     

Gr-凝聚环的分次FP-内射维数

引进了分次FP-内射维数，对Gr-凝聚环的分次FP-内射维数作了刻划，将Stentrom等人的若干工作推广到分次环上．     

HoYb:YVO4的上转换发光研究

研究了960nm激光激发下HoYb双掺钒酸钇晶体HoYb:YVO4的直接上转换增敏发光,发现了Ho3+离子的上转换发光现象,HoYb:YVO4晶体的上转换发光是5F5→5I8最强,而5S2→5I8相对小了一个数量级,这是由于YVO4晶体既有很强的振子强度又有很大的多声子无辐射弛豫造成的. 关键词： 上转换发光 直接增敏(敏化) 钒酸钇YVO4晶体 Ho3+离子     

Effect of oxygen exposure on the magnetic properties of ultrathin Co/Ge(1 1 1) films

Influences of oxygen exposure on the magnetic properties of Co/Ge(1 1 1) ultrathin films have been investigated by surface magneto-optic Kerr effect technique. As the oxygen exposure increases on Co/Ge(1 1 1) films, their magnetic properties could be modified. As an example for 15 ML Co/Ge(1 1 1) films, the coercivity increases from 730 to 920 Oe and the remanence Kerr intensity is reduced for 500 Langmuir (L) of oxygen exposure. Corresponding compositions analyzed by Auger electron spectroscopy measurement shows that the amount of oxygen on the surface layers increases with increasing the oxygen exposure time. Oxygen distributes on the topmost layers of the film. The adsorbed oxygen influences the electronic density of states of Co and results in the changes of the magnetic properties. Besides, the appearance of O/Co/Ge interface could modify the stress anisotropy, and as a result the coercivity of ultrathin Co/Ge(1 1 1) film is enhanced.